[Chemical composition] The composition does not change much, and sometimes a small amount of Sr and Ba replaces Ca.
[Crystal structure] orthorhombic system; 
a 0 =0.699 nm, b 0 =0.700 nm, c 0 =0.624 nm; Z=4.
[Form] Crystals are rare. Usually, it is elongated along the a-axis or the c-axis, and is sometimes in the form of a column. According to (011) contact twin or polycrystalline twin. The aggregate is fibrous, dense granular or massive (Figure H-20).
Figure H-20 anhydrite crystal
[Physical properties] white, often slightly light blue, light gray or light red, dyed red, color or gray by iron oxide or clay ; streaks white or light grayish white; crystal colorless and transparent; glass luster, solution The surface is pearly. Cleavage {010} is complete, {100}, {001} is medium ({100} is better than {001}). Hardness 3 to 3.5. The relative density is 2.8 to 3.0.
[Cause] anhydrite and the occurrence of major chemical deposition product is formed in a large number of salt lakes, often coexist with gypsum. Anhydrite is unstable under surface conditions and converted to gypsum.
Occasionally appeared in the hydrothermal veins and volcanic lava holes. In some sulphide deposits, there may be a small amount of oxidized zone (such as Northwest China).
[Characteristics] Identification and aromatic mineral barite its relatively low density, the cleavage directions (perpendicular to each other cleavage Group 3) and the optical constants of the phase difference; difference between the particulate calcium carbonate is magnesium HCl dropwise non-foaming; and The difference between gypsum is that the hardness is large and the nails are not immovable.
[Main use] It is roughly the same as plaster.
Trapezoidal Roofing Sheet Roll Forming Machine
Working principle:
steel strip is made into trapezoidal roofing sheet by machine through cold-bend forming technology.
Usage:
Trapezoidal roofing sheet produced by roll forming machine are widely used in construction, transportation and other industries. It is mainly used for roofing and wall of buildings, such as steel structures, airports, storehouses,etc.
Component:
1.Decoiler
2.Roll Forming System
3.Cutting Device
4.Hydraulic Station
5.PLC control system
Working Flow:
Loading coil – decoiling – guide feeding – main roll forming – hydrarlic cutting – finished products
Trapezoidal roofing sheet Roll Forming Machine Technique Parameters:
Processing material: aluzinc/galvanized steel/colored steel coil
Material thickness: 0.3-0.8mm
Main motor power: 4kw(can change as request)
Pump power: 4kw
Shaft diameter: 75mm and solid shaft
Forming steps: 15steps and more
Roller material: high grade 45# steel, hard Chromium plating
Main frame:300H steel
Medium plate thickness: 16mm
Speed:8-12m/min
Material of the cutting blade:Cr12
Control system: PLC computer control
Power supply: 380V, 3 Phase, 60Hz (can change as customers request)
Trapezoidal roofing sheet profile series:
Our Trapezoidal roofing sheet Roll Forming Machine can greatly simplifie the production process and improve production efficiency.
Welcome visit our Factory!
Trapezoidal Roofing Sheet Roll Forming Machine
Trapezoidal Roofing Sheet Roll Forming Machine,Sheet Crimp Machine,Roofing Sheet Roll Forming Machine,Trapezoidal Cold Roll Forming Machinery
CANGZHOU DIXIN ROLL FORMING MACHINE CO., LTD , https://www.hebeimachine.com